1.Dongyue Machinery Group is a company specialized in producing Sand Fly ash AAC BLOCK MACHINE,AAC PANEL MAKING MACHINE,The capacity is between 50000m3 to 300000m3 per year.
With technology cooperation with Germany company AAC CONCEPT,Our aac block machine inherits germany technology.So far we have 15 line of AAC block machine in Indonesia,10 lines in india,5 lines in Vietnam,2 lines in Buma,2 lines in Mongolia ,1 line in Kazakhstan ,1 one in Bulgaria
 
2.What is AAC?
AAC is a kind of light cellular silicate products. Main material based on Silicon materials ( sand, fly ash,gangue contains silicon)and Calcium(cement and lime),mix with foaming agent (Aluminium powder), after batching, mixing, pouring,pre-curing,cutting,stream(autocaled),and other process ,finally, get this light weight concrete products..  

 
3. fly ash aac plant raw material introduction
 
 
Fly-Ash:     A lot has been said about this raw material in this Project Profile itself. But this Raw material is freely available in Thermal Power plants. There are no taxes on this item whatsoever. Transportation charges are only to be attended by the entrepreneur.   
 
 
Sand:   Except fly ash,Sand can be the main material too.The requests is that the Silica content is above 69% .
 
Lime:     Active powered lime is a requirement for giving the real aeration to the product. In phase 1 we can aim to buy the active lime directly. In phase -2 we can think of having backward integration and making a lime powering unit at site to have a more competitive advantage, We can also think of a lime  burning klin inside the factory premises.   The project financials however have not considered  the costs of powering unit, and the lime kiln in this project.     Different qualities of lime are available, and depending on the raw materials, the mix design can be chosen to get the optimal quality of production.  
 
OPC cement.    This Project aims to utilize OPC cement as main binder material. It will give faster strength to the bricks, besides giving  improved consistent quality. It also ensures a better cost effectiveness for the same. Using OPC will be a standardized practice. The other prime advantages of using OPC (compared to other binders) is it's easy availability locally through nationwide Retail Network of Cement Companies.   
 
Gypsum:     This too is an industrial waste. This is available as an industrial byproduct of Fertilizer Plant. Gypsum is responsible to give long term strength to the Blocks.      
 
Aluminum Power.     Finely ground Aluminum power is used in very limited quantity ( less than 0.5%), so that it reacts with active lime, and silica in base material to make the aeration,
  (11) cement lime sand style aerated block raw material proportion  
4. fly ash aac plant production process
 

The Process of manufacture is simple t follow, and complex to implement. 
 
First, the Fly Ash is mixed with water, and made Slurry in a slurry mixture. If Sand is used as a base material, we need a ball mill to grind the sand to fine power. The slurry making process is same sand.  
 
After Slurry is made, the slurry is stored in slurry storage tank, where the slurry is constantly agitated. Care is taken to run the slurry storage tank all the time, so that is never settles down the particles. 
 
Then a weigh batcher weighs the Slurry, lime, OPC, Gypsum and aluminum power in preset quantities, and mixes thoroughly. The mixture also pours the mix into the Mould carried n the mould cart. The full pouring of the mixture is just enough to fill around 50% of the mould.   
 
Then the mould is kept in a warm chamber for 2 hours, so that the aeration and the light initial setting takes place.    Next process is de-molding process of the big block, in which a sophisticated overhead hoist takes the mould, demoulds the block.   
 
Next process is the level wire cutting of the Block, while the block passes on the cutting trolley through the series of wires. This process follows a vertical wire cutting where as the block remains stationary, and the cutter cuts the block vertically.   
 
The final cut blocks are Steam cured in autoclaves for 8 hours at 12 KG/Sq cm pressure, and 200D C